Silica Aerogel Click rate: Release time:2025-01-03 Information sources:Hangzhou Qiyao New Material Co.,Ltd.

Due to its low strength, brittleness and difficulty in forming, aerogel usually needs mechanical modification to obtain practical application value. The mechanical reinforcement of aerogel can be divided into inorganic reinforcement, polymer reinforcement and organic inorganic hybrid reinforcement.

Inorganic Enhancement

Using ethyl orthosilicate, dimethyl diethoxysilane and mullite fiber as raw materials, the aerogel thermal insulation composite was prepared by sol-gel, supercritical drying and high temperature cracking at 1200℃. The obtained aerogel composite has good formability. Using aluminum silicate fiber and glass fiber as skeleton materials, fiber composite Si02 aerogels were prepared by atmospheric drying. The two fiber composite Si02 aerogel materials are resistant to high temperature, have high fire and heat insulation properties, and the combustion performance reaches class A.

Polymer Reinforced

Polymer reinforcement is to introduce polymer into the skeleton or pore of aerogel material, and form organic cross-linked network with Si02 particles to enhance the effect. This method can significantly improve the integrity and mechanical properties of aerogel, and is an ideal reinforcement method. The properties of the aerogel are mainly determined by its internal pore structure. The mechanics and formability of crosslinked Si02 aerogel can be effectively controlled by selecting suitable polymer type and content. By combining hydrophilic PVA with superhydrophobic Si02 aerogel, a heat-insulating aerogel composite was prepared, which maintained the microporous structure of the aerogel well by using the special interfacial interaction. Alginic acid was introduced to the surface of Si02 particles, which effectively inhibited the collapse of Si02 aerogel due to surface tension during drying, and the composite aerogel was prepared with high surface area and porosity. The combustible organic polymer and Si02 strengthen the skeleton of the aerogel, greatly improve the toughness and formability of the material, but at the same time reduce the flame retardant property of the composite aerogel.

Organic and Inorganic Hybrid Enhancement

The mechanical properties of aerogel can be enhanced by forming the supporting skeleton of organic material and inorganic aerogel and using organic material with high mechanical strength as the carrier of brittle aerogel structure. The silica gel was enhanced by forming a nanoscale interpenetrating network containing silica gel skeleton and cellulose nanofiber network. The bacterial cellulose formed by Acetobacter xylosa growing on solid AGAR was then dried by gel and supercritical fluid to form an enhanced Si02 aerogel with low density, high specific surface area, high porosity and low thermal conductivity, and excellent bending and tensile properties. By adding clay material to the polyimide reinforced Si02 aerogel structure, the results show that the hydroxyl group on the clay surface can significantly enhance the modulus of the material and slightly reduce the specific surface area of the material through covalent and hydrogen bonding interactions with the gel network.


Copyright ? 2017 qiyaomaterial.com All Rights Reserved Copyright·Hangzhou Qiyao New Material Co.,Ltd. Zhejiang ICP No. 17034714-1
主站蜘蛛池模板: 色一欲一性一乱一区二区三区 | 中韩日欧美电影免费看 | a级网站| 亚洲骚片| 免费一级成人毛片 | 四虎永久影院永久影库 | 俺去操| 亚洲不卡视频 | 色www 永久免费网站 | 在线观看一二三区 | 丁香五六月婷婷 | 九九福利| 香港日本三级在线播放 | 久久 在线播放 | 伊人久久亚洲综合天堂 | 正在播放欧美 | 国产美女叼嘿视频免费看 | 伊人久久大香线蕉综合电影 | 国模大尺度人体一区 | bt天堂资源在线种子 | 亚洲高清一区二区三区四区 | 欧美三级在线 | 日本电影在线观看黄 | 欧美资源在线观看 | 初恋视频黄色 | 天天做天天玩天天爽天天 | 日韩毛片网站 | 亚洲日本高清 | 波多野结衣的毛片 | 国产伦精品一区二区三区高清 | 神马影院午夜在线 | 在线观看亚洲一区二区 | 久久精品亚洲精品国产色婷 | 成人男女啪啪免费观看网站 | 香蕉视频国产在线观看 | 萝l在线精品社区资源 | 天天躁狠狠躁 | 国产三级播放 | 亚洲国产精品丝袜在线观看 | 亚洲激情视频 | 国产精品嫩草影院午夜 |